WIDOCRYL-WT

Flexible Joint Compound

Designed for refurbishment and new construction
Over 50 years of waterproofing excellence

Product: WIDOCRYL-WT Flexible Joint Compound

Applications

Special Applications

WIDOPAN PRODUCTS ARE AVAILABLE FOR USE BY FULLY TRAINED & APPROVED INSTALLERS.

View Courses

Widopan Product

WIDOCRYL-WT Flexible Joint Compound

WIDOCRYL-WT Flexible Joint compound is specifically developed for floor movement joints in heavy load, high traffic areas such as warehouses, car parks, hangars and airport buildings.

With WIDOCRYL-WT, existing movement/expansion joints are eliminated, and the floor surface is left smooth. Thus removing the risk of trip hazards and deterioration associated with traditional expansion/movement joints.

WIDOCRYL-WT Flexible Joint compound is a highly flexible system that creates a virtually seamless joint that is antivibration and abrasion resistant.

Suitable for indoor and outdoor use, WIDOCRYL-WT is UV and chemical resistant, highly loadable and is trafficable 60 minutes after application.

When finished with WIDOCRYL-Topsiegel, the joint can be sealed with a colour of your choice.

Benefits of WIDOCRYL-WT

Creates a virtually seamless transition of the joint
UV & chemical resistant
Trafficable 60 minutes after application
Anti-vibration
Permanently elastic
Abrasion resistant & highly loadable
Cold applied – No heat required

Data Sheets

Product Information

Title	Extension	Size
WIDOCRYL-WT Product Data Sheet	pdf	382.62 KB
WIDOCRYL-WT Safety Data Sheet	pdf	234.43 KB

Product Infromation

WIDOCRYL-WT Flexible Joint Compound

WIDOCRYL-WT is the liquid plastic system which is used as flexible joint closing compound for joints with low dynamic movements. The material basis of WIDOCRYL-WT is urethane-modified methyl methacrylate resin.

The cured WIDOCRYL-WT results in a highly flexible joint closing with outstanding high crack binding properties. WIDOCRYL-WT is resistant to static and shock-loaded punctual loadings and bridges tensile stress as well as movements in the substructure. In addition, WIDOCRYL-WT is highly resistant to chemicals and abrasion and it is UV-stable and weatherproof.

With correct priming, WIDOCRYL-WT adheres to al-most any surface.

PLEASE note for application of the WIDOCRYL-WT:

The PD-Powder is mixed into the fluid component WIDOCRYL-WT (mixing ratio: PD-Powder 1kg : WIDOCRYL-WT 2kg)

To make sure that the material will cure properly, each layer thickness should not exceed 25 mm.

Further details can be found in the safety data sheet.

Basis

Urethane-modified methyl methacrylate resin

Density/Specific weight

1.23 g/cm³

Curing with Hardener (at +20°C)

Walkable after 60 min.

Technical characteristics (cured state)
(Sample tested at +20°C)

Tensile strength: 5.0 MPa
Elongation: 330%
Modulus of elasticity: 8.3 MPa
Dynamic crack-bridging: >5 mm
Samples kept at –30°C for 24 hours before testing
Tensile strength: 4.3 MPa
Elongation: 315%
Modulus of elasticity: 225 MPa
Dynamic crack-bridging: > 5 mm